CE-355
White granular
| Quantity: | |
|---|---|
Technical parameter
Model No.: CE-355
Chemical composition: sodium bicarbonate salt complex
Carrier resin: LDPE
Appearance: white granular
Decomposition temperature: 170-200 ℃
Gas production (STP): 35-45 ml/g
Application Features:
●Controllable decomposition speed, dynamic matching of various processing techniques
The cells are uniform and fine, and the epidermis is smooth and free of mottled
●Eliminate plastic injection shrinkage
●Short injection molding cycle and reduce product weight
●Food grade environmental protection, food contact safety
Recommended dosage:
0.5-2.0%(injection)
1.0-3.0% (extrusion)
Package & Storage
It must be stored in a cool, dry place, and kept away from hot steam pipes and fire sources to avoid direct sunlight. It is strictly prohibited to direct contact with acid and alkali. The auxiliary is packed by 25kg per bag.
Foaming masterbatch is a high-performance polymer additive that can be used to improve the physical properties of plastics. It is available in a wide range of colors and can be customized to meet the specific needs of your application. Foaming masterbatch can be used to improve the strength, stiffness, and impact resistance of plastics, as well as to reduce weight and volume.
Foaming masterbatch is a polymer additive that can be used to create a variety of foamed products with desired properties. The main advantage of foaming masterbatch is its ability to produce products with improved mechanical and thermal properties. Foaming masterbatch can also be used to improve the dimensional stability of products and to reduce weight.
Technical parameters of foaming masterbatch
1. Melt flow rate (MFR, g/10min): 2~12
2. Density (g/cm3): 0.92-0.96
3. Particle size (μm): 20-80
4. Appearance: White or light yellow fine powder, no foreign matter visible to the naked eye
5. Thermal conductivity coefficient (W/(m·K)): 0.035~0.045
6. Vicat softening temperature (℃): 105~115
7. Melting point (℃): 115~125
8 Decomposition temperature (℃): 200
Foaming masterbatch is a versatile product that can be used in a variety of applications. Here are just a few examples of how foaming masterbatch can be used:
-Injection molded products: Foaming masterbatch can be used to produce injection molded products with a variety of different textures and appearances.
-Extruded products: Foaming masterbatch can also be used to produce extruded products such as pipe and tubing.
-Thermoformed products: Thermoformed products such as cups and containers can also be made using foaming masterbatch.
-Film and sheet: Film and sheet products can also be made using foaming masterbatch.
Technical parameter
Model No.: CE-355
Chemical composition: sodium bicarbonate salt complex
Carrier resin: LDPE
Appearance: white granular
Decomposition temperature: 170-200 ℃
Gas production (STP): 35-45 ml/g
Application Features:
●Controllable decomposition speed, dynamic matching of various processing techniques
The cells are uniform and fine, and the epidermis is smooth and free of mottled
●Eliminate plastic injection shrinkage
●Short injection molding cycle and reduce product weight
●Food grade environmental protection, food contact safety
Recommended dosage:
0.5-2.0%(injection)
1.0-3.0% (extrusion)
Package & Storage
It must be stored in a cool, dry place, and kept away from hot steam pipes and fire sources to avoid direct sunlight. It is strictly prohibited to direct contact with acid and alkali. The auxiliary is packed by 25kg per bag.
Foaming masterbatch is a high-performance polymer additive that can be used to improve the physical properties of plastics. It is available in a wide range of colors and can be customized to meet the specific needs of your application. Foaming masterbatch can be used to improve the strength, stiffness, and impact resistance of plastics, as well as to reduce weight and volume.
Foaming masterbatch is a polymer additive that can be used to create a variety of foamed products with desired properties. The main advantage of foaming masterbatch is its ability to produce products with improved mechanical and thermal properties. Foaming masterbatch can also be used to improve the dimensional stability of products and to reduce weight.
Technical parameters of foaming masterbatch
1. Melt flow rate (MFR, g/10min): 2~12
2. Density (g/cm3): 0.92-0.96
3. Particle size (μm): 20-80
4. Appearance: White or light yellow fine powder, no foreign matter visible to the naked eye
5. Thermal conductivity coefficient (W/(m·K)): 0.035~0.045
6. Vicat softening temperature (℃): 105~115
7. Melting point (℃): 115~125
8 Decomposition temperature (℃): 200
Foaming masterbatch is a versatile product that can be used in a variety of applications. Here are just a few examples of how foaming masterbatch can be used:
-Injection molded products: Foaming masterbatch can be used to produce injection molded products with a variety of different textures and appearances.
-Extruded products: Foaming masterbatch can also be used to produce extruded products such as pipe and tubing.
-Thermoformed products: Thermoformed products such as cups and containers can also be made using foaming masterbatch.
-Film and sheet: Film and sheet products can also be made using foaming masterbatch.